Epoxy WHG Color AS

The substrate must be firm, dimensionally stable, capable of bearing loads and free of loose constituents, dust, oil, grease, rubber marks and other substances that could interfere with adhesion.

The adhesive pull strength of the surface after priming must be at least 1.5 N/mm² on average (smallest single value min. 1.0 N/mm²), compressive strength at least 25 N/mm².

Suitable Remmers epoxy primers, epoxy scratch coats or epoxy mortars must always be used.

For works within the framework of the general building inspectorate approval, the substrates must correspond to the requirements of the approval and the system products mentioned therein must be used.

Before the application of the product a smooth surface must be produced, e.g. with a scratch coat.

Refer to the current Technical Data Sheet for detailed information on the single products.

Epoxy Conductive must be applied according to the current Technical Data Sheet as transverse conducting layer.

Add the entire quantity of the hardener (component B) to the base compound (component A).

Mix thoroughly with a slow-speed electric mixer
(approx. 300 - 400 rpm).

Pour the mixture into a separate container and mix again thoroughly.

Mix for at least 3 minutes.

Insufficient mixing is indicated by streaks forming.

As a general principle, higher temperatures will reduce and lower temperatures will increase the times stated.

Toothed trowel, notched spreader, spiked roller (metal), rubber scraper, epoxy roller, suitable mixing apparatus

More detailed information can be found in the Remmers Tool Programme.

Clean tools, equipment and splashed material immediately while fresh with V 101.

Take suitable protective and waste disposal measures when cleaning.

If stored unopened in its original container in a cool, dry place and protected against frost, the product will keep for at least 12 months.

See application examples

Pour the material onto the prepared substrate and then distribute using a suitable tool, e.g. a notched trowel or notched scraper.

Afterwards roll over with a (metal) spiked roller.

min. 1.5 kg/m² binder

Pour the unfilled material on the previously prepared surface, distribute with a suitable toothed trowel/squeegee and, if required, roll over with a spiked roller.

Broadcast an excess of suitable silicon carbide or Ceramix Conduct 04/08 into the wet base layer.

Remove any loose, excess material after hardening.

min. 0.8 kg/m² binder and
5 - 6 kg/m² silicon carbide or Ceramix Conduct 04/08 (including excess)

Pour the material onto the prepared surface, spread evenly using a rubber scraper, then roll crossways using a suitable epoxy roller.

approx. 0.6 - 0.7 kg/m² binder

Unless otherwise specified, all of the values and application rates given above have been determined under laboratory conditions (20 °C) using standard colours. Slight deviations from these values may arise if the product is worked with on site.

The stated approximate application quantities refer to smooth, level substrates.

When coating continuous surfaces, only use materials with the same batch number as slight differences in colour, gloss and texture may occur.

Carbon fibres are visible on the surface. Because of the way the coating is applied, the carbon fibres may bundle.

Due to the black transverse conducting layer, poorly covering colours are not to be used.

When used as a top seal, the inherent colour of the granules may limit the opacity of light shades.

Before the application of the covering layer, the correct functioning of the transverse conducting layer and of the connections must be proved and registered in a measurement report.

The use of the product as a blinding layer or top seal does not form part of the AbZ certification (Z-59.12-303).

Low levels of air humidity can cause a higher discharge resistance, uneven or thicker layers can even lead the coating to not be conductive at all.

Application of the mixture by toothed trowel/toothed spreader. If the product is applied with a smoothing trowel/screed levelling tool, trowel marks may be visible on the finished surface.

In case of repairs on the surface or working up to existing surfaces, there will be a visible transition in appearance and texture.

Abrasive mechanical loads leave traces of wear.

Exposure to vehicles with metal or polyamide tyres as well as dynamic concentrated loads can cause faster wearing of the coating.

Epoxy resins are generally not colourfast when exposed to UV light or weather.

Further notes on working, system construction and maintenance of the listed products can be found in the latest Technical Data Sheets and the Remmers system recommendations.

Larger quantities of leftover product should be disposed of in the original containers in accordance with the applicable regulations. Completely empty, clean containers should be recycled. Do not dispose of together with household waste. Do not allow to enter the sewage system. Do not empty into drains.

For professional users only!

For further information on the safety aspects of transporting, storing and handling the product and on disposal and environmental matters, please see the current Safety Data Sheet and the brochure entitled "Epoxy Resins in the Construction Industry and the Environment", issued by Deutsche Bauchemie e.V. (3rd edition 2022).